Product properties
DSCTJ 6104PTI is low-density inflaming retarding unsaturated polyester resin. The resin contains accelerant and aluminum hydroxide.
Main application
DSCTJ 6104PTI is a filled flame-retarded resin, and its filling system is suitable for hand lay-up process. It is a high inflaming retarding resin, with good operating process and mechanical properties.
Certification:
UL 94 , V-0
(The above certification is based on 6104PTI, production of test panels with hand lay-up process)
Note: gel time, 100g resin was added 1.5g M-50 (AKZO-Nobel)
Glass fiber reinforced material performance
Item Performance
value Test Method
Tensile strength *** 110 GB/T 1447-2005
Tensile Modulus *** 7400 GB/T 1447-2005
Bending strength *** 175 GB/T 1449-2005
Flexural modulus *** 8700 GB/T 1449-2005
I***ct strength kJ/m2 160 GB/T 1451-2005
Barcol hardness 50 GB/T 3854-2005
(The above data is based on 6104PTI hand lay-up fiberglass fabrication test panel)
Instructions and Precautions:
1. In order to ensure uniform DSCTJ 6104PTI system, hand lay-up process should be carried out after stirring well with a stirrer.
2. The curing agent shall be within the validity period.
Storage conditions:
1. Before using, the resin be stored in a dry room in the original packaging (to avoid the wear between barrel and barrel).
2. The high temperature and light exposure will be significantly reduced storage life, so storage should avoid direct sunlight and away from heat.
3. If exposed to air DSCTJ 6104PTI will be crust, so it should be hand lay-up after stirring well and then curing.
|
| Company: |
Bolanshuoke Technology Development Co., Ltd.
|
| Contact: |
Mr. Rex Zeng |
| Address: |
Dongli District |
| Postcode: |
|
| Tel: |
0086-022-86728451 |
| Fax: |
0086-022-86728452 |
| E-mail: |
|
|
|
|
Home