Medium Temperature Curing of Epoxy Resin System
|
| Supply Ability: |
|
| Related proudcts |
epoxy resin, wettability, |
| Specifications |
DSJW6966A |
| Price Term: |
|
| Port of loading: |
|
| Minimum Order |
|
| Unit Price: |
|
|
This resin system has good wettability, medium curing activity and moderate viscosity. Molded product, with excellent mechanical properties and high toughness, good corrosion resistance, it’s overall performance reached and exceeded similar imported epoxy resin, is suitable for hand lay-up, vacuum infusion, resin transfer molding and other processes. Widely used in the manufacture of high-grade auto parts, megawatt-class wind turbine blades (38 m -62 m), aero***ce parts and military and civil ships, composite mold and other fields.
I. Resin system
DSJW8966A resin
Resin viscosity (25 â„?: 1100***s
Density: 1.122-1.128g / cm3
Flash Point: 220 â„?
DSJW6966B curing agent
Viscosity (25 â„?: 11***s
Density: 0.942-0.948g / cm3
Flash Point:> 200 â„?
II. Mixing Characteristics
Weight ratio: DSCW6966A Epoxy resin: DSJW6966B Curing agent: = 100: 30
Shelf Life
Table 1 Shelf Life�5℃）
Dosage（gram�Time（min�
100 310
Gel Time
Temperature（℃�Gel time (min)
40 157
60 55
70 22
Curing property
Curing temperature（℃�Curing time (hour) starting point temperature（℃�starting point temperature（℃�
60 6 70 76
70 6 76 80
III. Mechanical properties:
Curing system: 70â„?curing temperature, 6 hours of curing time
1. Casting body performance:
Tensile properties (ISO 527-2)
Tensile strength: �3***
Tensile modulus: �.9GPa
Tensile Strain at break: �.0%
Compression properties (GB / T 1041-92)
Compressive strength: �0***
Bending properties (ISO 178)
Bending strength: �05***
Flexural modulus: �.9GPa
2. Composites properties (glass fiber uniaxial UD1200)
0 ° tensile properties (ISO 527-5)
Tensile strength: �30***
Tensile modulus: �4Gpa
0 ° compression performance (ISO 14126)
Compressive strength: �00***
Compression modulus: �2Gpa
Operation Information
1. Before mixing
Remove dirt, grease and moisture on the mold surface
2. Mixing
The resin and hardener should be mixed pro ra |
| Company: |
Bolanshuoke Technology Development Co., Ltd.
|
| Contact: |
Mr. Rex Zeng |
| Address: |
Dongli District |
| Postcode: |
|
| Tel: |
0086-022-86728451 |
| Fax: |
0086-022-86728452 |
| E-mail: |
|
|
|
|
Home